Project:Airlag chess figures

From CoMakingSpace Wiki
Revision as of 14:22, 18 October 2019 by Airlag (talk | contribs)
(diff) ← Older revision | Latest revision (diff) | Newer revision → (diff)
Jump to navigation Jump to search
ProjectInfoBox

Chess Figures

Airlag chess figures 20191004 185618.png
Status: in progress
Release Date: christmas time - maybe
Initiator: Airlag
Materials Used: styrene foam, silicone rubber, alkali activates silicates
Tools Used: sharp knife, drying oven
Approx. Cost: 80 €


This is my first project I'm doing in the CoMakingSpace for real. I thought about a few other projects but those never made it past the thinking and sketching part.

A few months ago I stumbled over some information about Geopolymers in the internet:

and several more. (In this context it is irrelevant whether it is historical correct if the pyramids were partly built using concrete or not)

The recipe varies from website to website. Wiki explains that there is a wide variety of ingedients that can replace each other. Therefore I started my own experimental research with available or easily accessable materials.

One of the ingredients is soda lye (NaOH). This chemical is corrosive.

The materials and chemicals aren't expensive. The most expensive is definitely the silicone rubber. I'm not finished jet but I expect there will be lots of leftovers.

Portland Cement Free Concrete

Trial 1

the activator:
6g water
add 4g NaOH slowly because the chemical reaction produces heat
add 25g sodium silicate

the aggregate:
185g sand (unknown origin, turned out it contained lots of limestone)
add 100g Zeolith powder

add the activator to the aggregate

Zeolith is a relatively cheap mineral. I ordered some powder. I got granumate instead. I tried anyways.

The resulting mixture was in no way pourable. I tried to pack it, then I let the chemistry magic do its job.

Airlag chess figures 20190821 173653.png Airlag chess figures 20190821 174346.png

After a week it was hard but porose and crumbly.

Airlag chess figures 20191010 152328.png

Trial 2

the activator: same as above
6g water
add 4g NaOH
add 25g sodium silicate

the aggregate:
200g trass powder (Trass is the local name of a volcanic tuff occurring in the Eifel, Germany)
100g white sand from a pet shop

add the activator to the aggregate

The resulting mixture looked like moist sand but was very squashy. The mixture was not pourable.
After a week it was still moist and squashy.
Baking it in a drying oven at 80°C for 3 hours turned it to a rock.
After another week I discovered that the reference body shows some cracks.
Several weeks later it seems to sweat out some kind of nearly white powder. The cracks seem to get smaller.

Airlag chess figures 20190906 170024.png Airlag chess figures 20191010 152545.png

Trial 3

the activator: same as above just 4 times more of it
24g water
add 16g NaOH
add 100g sodium silicate

the aggregate:
200g trass powder
add 100g white sand

add the activator to the aggregate

The resulting mixture is creamy but still not pourable. However, I tried this mixture for a first atempt on the chess figures (see below).
This time I put it immediately into the drying oven at about 60°C for 3 hours. The resulting reference body seemed hard but it isn't entirely. Hitting the edge of a table caused a dent in the reference body. One week later nothing has changed. The hardened material is as durable as chalk.

Airlag chess figures 20190914 134952.png Airlag chess figures 20191010 152704.png

Trial 4

the activator:
30g water
add 18g NaOH
add 40g sodium silicate

the aggregate:
140g trass powder
add 200g white sand
add 4g titan white (just for the color)
add 80g water

add the activator to the aggregate

This recipe was from another web page. In my opinion there are two main differences. The mix ratios differ greatly. There is way more water involved as needed to dissolve the lye. And the aggregate is mixed with water before the activator is added.

The aggregate was creamy after mixing with water. When I added the activator it turned into a pourable liquid. That looked promising - at first.

I filled the cases and baked them in the drying oven at 70°C for about two days. The result was not durable at all. It crumbled literally at sight.

The Chess Figures

I want to make chess figures out of liquid stone.
For this I need casts.
To make casts I need prototype figures.

I decided to use styrene foam, a penknife and glue to create my prototypes. I had some square meters of 5mm panels lying around. So I used that material. It's very easy to cut but it's hard to carve tiny details. The material tends to crumble if you don't use the sharpest possible knife.
I wasn't satisfied with the first set of figures, so I made a second set.

Next I created small boxes for each figure out of the same material. I glued one figure to the bottom of each box, then I poured silicone rubber in the box. Two hours later I removed the box and cut the silicone rubber in half. After removing the remains of the prototype figure the reusable cases for the stone figures are finished.

I didn't make much pictures. Shame on me. I only have this picture of the first set of prototype figures.

Airlag chess figures 20191010 165559.png

Figures Trial 1 from Material Trial 3

Material Trial 3 seemed promising enough, so I poured it as good as possible into the silicone cases. The material was creamy, not liquid. So I ended up with several bubbles. The horse has no chin. The queen broke in half. Anyways, it's the first attempt. So here are the results.

Airlag chess figures 20191004 190213.png Airlag chess figures 20191004 190141.png Airlag chess figures 20191004 190113.png Airlag chess figures 20191004 190047.png Airlag chess figures 20191004 185850.png

Airlag chess figures 20191004 185636.png Airlag chess figures 20191004 185619.png

And then I threw them away. Next try will be better :-)

Figures Trial 2 from Material Trial 4

A total fail.

Airlag chess figures 20191013 161728.png